Organic compound and organic light emitting diode device including the same

ABSTRACT

Disclosed are a novel organic compound and an organic light emitting diode device using the same. More particularly, a novel organic compound having electrical stability, high charge transport capability, and light emitting performance, high glass transition temperature and being capable of preventing crystallization, and an organic light emitting diode device including an organic layer including the same are disclosed.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to and the benefit of Korean Patent Application No. 10-2013-0040656 filed in the Korean Intellectual Property Office on Apr. 12, 2013, the entire contents of which are incorporated herein by reference.

BACKGROUND

1. Field

An organic compound and an organic light emitting diode device are disclosed.

2. Description of the Related Technology

Recently, demand for reduced size and thickness of a monitor, a television, or the like has promoted replacement of a cathode ray tube (CRT) with a liquid crystal display (LCD). However, the liquid crystal display (LCD) does not only need a separate backlight as a non-emissive device but is also limited in terms of a response speed, viewing angle, and the like. Recently, organic light emitting diode devices have been contemplated as a display device to overcome such limits. The organic light emitting diode device is a self-light emitting display device having a wide viewing angle, improved contrasts and a fast response time. An organic light emitting diode device includes two electrodes and an emission layer disposed therebetween and emits light when electrons injected from one electrode are combined with holes injected from the other electrode and thus, form excitons and emit energy.

SUMMARY

One embodiment provides a novel organic compound that is applicable to an organic light emitting diode device.

Another embodiment provides an organic light emitting diode device including the organic compound.

One embodiment provides an organic compound represented by the following Chemical Formula 1.

In the above Chemical Formula 1,

R₁ and R₂ may independently be hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring,

R₃ to R₅ may independently be hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof,

n may be an integer ranging from 0 to 2, and

Ar₁ and Ar₂ may independently be a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.

Specifically, the R₁ and R₂ may independently be a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, and

Ar₁ and Ar₂ may independently be a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.

More specifically, the R₁ and R₂ may independently be a substituted or unsubstituted C₁ to C₃₀ alkyl group, or a substituted or unsubstituted C₁ to C₃₀ aryl group, or R₁ and R₂ are linked to each other to form a ring, and

Ar₁ and Ar₂ may independently be a substituted or unsubstituted phenyl group, a substituted or unsubstituted biphenyl group, a substituted or unsubstituted terphenyl group, a substituted or unsubstituted naphthalene group, a substituted or unsubstituted anthracene group, a substituted or unsubstituted phenanthrene group, a substituted or unsubstituted pyrene group, a substituted or unsubstituted fluorene group, a substituted or unsubstituted carbazole group, a substituted or unsubstituted dibenzofuran, a substituted or unsubstituted dibenzothiophene, a substituted or unsubstituted pyridine group, or a combination thereof.

The compound represented by the above Chemical Formula 1 may be an organic compound including at least one selected from the compound listed in the following Group 1.

Another embodiment provides an organic light emitting diode device that includes an anode, a cathode, and an organic layer interposed between the anode and cathode, wherein the organic layer includes the organic compound represented by the above Chemical Formula 1.

The organic layer may include an emission layer, and the organic compound represented by the above Chemical Formula 1 may be included in the emission layer.

The emission layer may further include anthracene, arylamine, styrene, a derivative thereof, or a combination thereof.

The emission layer may include the organic compound represented by the above Chemical Formula 1 as a fluorescent or phosphorescent host.

The organic layer may include an emission layer and an auxiliary layer interposed between the emission layer and the cathode, and the organic compound represented by the above Chemical Formula 1 may be included in the auxiliary layer.

The emission layer may include anthracene, arylamine, styrene, a derivative thereof, or a combination thereof.

Other embodiments are included in the following detailed description.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 shows the structure of an organic light emitting diode device according to one embodiment.

DETAILED DESCRIPTION

Hereinafter, the present disclosure will be described more fully hereinafter with reference to the accompanying drawings, in which example embodiments of this disclosure are shown. However, this disclosure may, however, be embodied in many different forms and is not construed as limited to the example embodiments set forth herein.

In the drawings, the thickness of layers, films, panels, regions, etc., are exaggerated for clarity. Like reference numerals designate like elements throughout the specification. It will be understood that when an element such as a layer, film, region, or substrate is referred to as being “on” another element, it may be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.

As used herein, when a definition is not otherwise provided, the term “substituted” refers to one substituted with a substituent selected from deuterium, a C₁ to C₃₀ alkyl group, a C₆ to C₃₆ aryl group, a C₂ to C₃₀ heteroaryl group, a C₁ to C₃₀ alkoxy group, a C₂ to C₃₀ alkenyl group, a C₆ to C₃₀ aryloxy group, a C₃ to C₄₀ silyloxy group, a C₁ to C₃₀ acyl group, a C₂ to C₃₀ acyloxy group, a C₂ to C₃₀ heteroaryloxy group, a C₁ to C₃₀ sulfonyl group, a C₁ to C₃₀ alkylthiol group, a C₆ to C₃₀ arylthiol group, a C₁ to C₃₀ heterocyclothiol group, a C₁ to C₃₀ phosphoric acid amide group, a C₃ to C₄₀ silyl group, NRR′ (wherein, R and R′ are each independently a substituent selected from hydrogen, a C₁ to C₃₀ alkyl group and a C₆ to C₃₀ aryl group), a carboxyl group, a halogen, a cyano group, a nitro group, an azo group, a fluorene group, and a hydroxy group, instead of at least one hydrogen.

The C₆ to C₃₆ aryl group, C₂ to C₃₀ heteroaryl group, and fluorene group may be further substituted with a substituent selected from deuterium, a halogen, a cyano group, a methyl group, a trifluoromethyl group, and a phenyl group.

As used herein, when a definition is not otherwise provided, the term “hetero” refers to 1 to 3 heteroatoms selected from N, O, S, and P, and remaining carbon in one ring.

As used herein, the “organic layer” may refer to a layer including an organic material, but the organic layer is not a layer consisting of an organic material, may include an inorganic material, a metal complex, and the like as well as an organic material, and may include at least one layer.

Representative groups in the chemical formulae of the present embodiments are defined as follows (carbon numbers of substituents are not limited and do not limit characteristics of substituents).

The unsubstituted C₁ to C₃₀ alkyl group may be linear and branched, and non-limiting examples thereof may be methyl, ethyl, propyl, isobutyl, sec-butyl, pentyl, iso-amyl, hexyl, heptyl, octyl, nonyl, dodecyl, and the like.

The unsubstituted C₂ to C₃₀ alkenyl group may have at least one carbon double bond in the middle or terminal end of the unsubstituted alkyl group. Examples thereof may be ethenyl, propenyl, butenyl, and the like.

The unsubstituted C₂ to C₃₀ alkynyl group may have at least one carbon triple bond in the middle or terminal end of the unsubstituted alkyl group. Examples thereof may be acetylene, propylene, phenylacetylene, naphthylacetylene, isopropylacetylene, t-butylacetylene, diphenylacetylene, and the like.

The unsubstituted C₃ to C₃₀ cycloalkyl group may refer to a cyclic alkyl group having 3 to 30 carbon numbers.

The unsubstituted C₁ to C₃₀ alkoxy group may refer to —OA (wherein, A is the above-described unsubstituted C₁ to C₃₀, and non-limiting examples may be methoxy, ethoxy, propoxy, isopropyloxy, butoxy, pentoxy, and the like.

The unsubstituted C₆ to C₃₀ aryl group may refer to a carbocycle aromatic system having at least one ring. The aryl group may have two or more rings, which may be fused or linked through a single bond and the like. The term aryl may include an aromatic system such as phenyl, naphthyl, anthracenyl, and the like. The unsubstituted C₆ to C₃₀ C₆ to C₃₀ aryl group may be selected from a phenyl group, a tolyl group, a naphthyl group, an anthracenyl group, a terphenyl group, a phenanthrenyl group, a pyrenyl group, a diphenylanthracenyl group, a dinaphthylanthracenyl group, a pentacenyl group, a bromophenyl group, a hydroxyphenyl group, a stilbene group, an azobenzenyl group, and a ferrocenyl group.

The unsubstituted C₂ to C₃₀ heteroaryl group may include 1, 2 or 3 heteroatoms selected from N, O, S, and P. The heteroaryl group may have two or more rings, which may be fused or linked through a single bond and the like. Examples of the unsubstituted C₂ to C₃₀ heteroaryl group may be selected from a pyrazolyl group, an imidazolyl group, an oxazolyl group, a thiazolyl group, a triazinyl group, a triazolyl group, a tetrazolyl group, an oxadiazolyl group, a thiadiazolyl group, a pyridinyl group, a pyridazinyl group, pyrimidinyl group, a triazinyl group, a carbazolyl group, an indolyl group, a quinolinyl group, an isoquinolinyl group, a thiophene group, a dibenzothiophene group, a dibenzofuran group, and a benzimidazolyl group.

The unsubstituted C₆ to C₃₀ aryloxy group may refer to —OA₁, wherein A₁ is the same functional group as the C₆ to C₃₀ C₆ to C₃₀ aryl group except carbon numbers. Examples of the aryloxy group may include a phenoxy group, and the like.

The unsubstituted C₆ to C₃₀ arylthio group may refer to —SA₁, wherein A₁ is the same functional group as the C₆ to C₃₀ aryl group except carbon numbers. Examples of the arylthio group may include a benzenethio group, a naphthylthio group, and the like.

Hereinafter, one embodiment and another embodiment are described in detail.

An organic compound according to one embodiment is represented by the following Chemical Formula 1:

In the above Chemical Formula 1,

R₁ and R₂ may independently be hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring,

R₃ to R₅ may independently be hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof,

n may be an integer ranging from 0 to 2, and

Ar₁ and Ar₂ may independently be a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.

Specifically, the R₁ and R₂ may independently be a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, Ar₁ and Ar₂ are each independently a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.

More specifically, the R₁ and R₂ may independently be a substituted or unsubstituted C₁ to C₃₀ alkyl group, or a substituted or unsubstituted C₁ to C₃₀ aryl group, or R₁ and R₂ are linked to each other to form a ring,

Ar₁ and Ar₂ may independently be a substituted or unsubstituted phenyl group, a substituted or unsubstituted biphenyl group, a substituted or unsubstituted terphenyl group, a substituted or unsubstituted naphthalene group, a substituted or unsubstituted anthracene group, a substituted or unsubstituted phenanthrene group, a substituted or unsubstituted pyrene group, a substituted or unsubstituted fluorene group, a substituted or unsubstituted carbazole group, a substituted or unsubstituted dibenzofuran, a substituted or unsubstituted dibenzothiophene, a substituted or unsubstituted pyridine group, or a combination thereof.

According to one embodiment, the organic compound represented by the above Chemical Formula 1 may function as a light emitting material or an electron transport material for an organic light emitting diode device.

The compound represented by the above Chemical Formula 1 may be, for example, a blue light emitting material, but is not limited thereto. The compound represented by the above Chemical Formula 1 includes at least one fused ring inside a molecule and thus, may increase a glass transition temperature (Tg) and a melting point and thereby, decrease Joule heat generated in an organic layer, between organic layers, and between the organic layer and a metal electrode and/or deterioration due to thermal stress at a high temperature when applied to an organic light emitting diode device.

Accordingly, the organic compound represented by the above Chemical Formula 1 may increase durability of the organic light emitting diode device during storage and operation. In addition, the organic compound represented by the above Chemical Formula 1 has an improved molecular film due to introduction of a substituent such as a fluorene group and the like and may improve characteristics of the organic light emitting diode device.

Examples of the compound represented by the above Chemical Formula 1 may be at least one compound listed in the following Group 1 (compounds represented by Chemical Formulae 2 to 70), but are not limited thereto. The compounds listed in the following Group 1 (compounds represented by Chemical Formulae 2 to 70) may be used singularly or in a mixture of at least two, and may be used in a mixture of another compound.

Hereinafter, an organic light emitting diode device including the organic compound according to one embodiment is described referring to FIG. 1.

FIG. 1 is a cross-sectional view of an organic light emitting diode device according to one embodiment.

Referring to FIG. 1, the organic light emitting diode device according to one embodiment includes an anode 1, a cathode 2 facing the anode 1, and an organic layer 10 interposed between the anode 1 and cathode 2.

The substrate (not shown) may be disposed on the side of anode 1 or on the side of cathode 2. The substrate may be made of an inorganic material such as glass or an organic material such as polycarbonate, polymethylmethacrylate, polyethyleneterephthalate, polyethylenenaphthalate, polyamide, polyethersulfone, or a combination thereof, silicon wafer, and the like.

One of the anode 1 and cathode 2 may be a transparent electrode, and the transparent electrode may comprise, for example conductive oxide such as indium tin oxide (ITO), indium zinc oxide (IZO), tin oxide (SnO₂), zinc oxide (ZnO), or a combination thereof, or a metal such as Al, Ag, or Mg in a thin thickness.

The organic layer 10 includes an emission layer 5, a hole auxiliary layer 3 interposed between the anode 1 and emission layer 5, and an electron auxiliary layer 4 interposed between the cathode 2 and emission layer 5. However, at least one of the hole auxiliary layer 3 and electron auxiliary layer 4 may be omitted.

The emission layer 5 may include the above-described organic compound. The organic compound may be used singularly or in a mixture and may be used in a mixture of another organic material. When the organic compound is mixed with another organic material, it may be function as a fluorescent or phosphorescent host, and may include well-known dopants.

A red dopant may include PtOEP, Ir(piq)₃, Btp₂Ir(acac), DCJTB, and the like, but is not limited thereto.

A green dopant may include Ir(ppy)₃(ppy=phenylpyridine), Ir(ppy)₂(acac), Ir(mpyp)₃, C545T, and the like, but is not limited thereto.

A blue dopant may include F₂Irpic, (F₂ppy)₂Ir(tmd), Ir(dfppz)₃, ter-fluorene, 4,4′-bis(4-diphenylaminostyryl)biphenyl (DPAVBi), 2,5,8,11-tetra-ter-butyl perylene (TBP), and the like, but is not limited thereto.

The dopant may be included in an amount of about 0.1 to about 15 parts by weight based on 100 parts by weight of emission layer forming material (i.e., total weight of the host and dopant is 100 parts by weight), without limitation.

The emission layer 5 may further include anthracene, arylamine, styrene, a derivative thereof, or a combination thereof as well as the above-described organic compound.

At least one hydrogen atom of the anthracene compound, arylamine compound or styrene compound may be substituted with the same substituent as that of the C₁ to C₃₀ alkyl group. The arylamine may be a C₅ to C₃₀ arylamine group, and may include an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group.

The emission layer 5 may emit white by a combination of red, green and blue three primary colors, and the combination of colors may be implemented by combination of adjacent sub-pixels to emit white or stack in a vertical direction to emit white.

The electron auxiliary layer 4 may be interposed between the emission layer 5 and cathode 2 to increase electron mobility. The electron auxiliary layer 4 may include at least one selected from, for example an electron injection layer (EIL), an electron transport layer (ETL), and a hole blocking layer.

The electron auxiliary layer 4 may include the above-described organic compound. When the electron auxiliary layer 4 includes the above-described organic compound, the emission layer 5 may include, for example anthracene, arylamine, styrene, a derivative thereof, or a combination thereof.

The hole blocking layer material is not particularly limited, and may include any general hole blocking layer materials. For example, an oxadiazole derivative, a triazole derivative, a phenanthroline derivative, Balq, BCP, and the like may be used.

The electron transport layer (ETL) material may be the organic compound represented by Chemical Formula 1 as above-described. Any general electron transport layer (ETL) forming material may be also used. For example, a quinoline derivative, particularly well-known material such as tris(8-quinolinolate)aluminum Alq₃, TAZ, Balq, and the like may be used, without limitation.

An electron transport layer (ETL) of an organic light emitting diode device according to another embodiment may include an electron transport organic compound and a metal-containing material. Non-limiting examples of the electron transport organic compound may include DNA (9,10-di(naphthalen-2-yl)anthracene); and an anthracene-based compound such as the following compounds 101 and 102, but are not limited thereto.

The metal-containing material may include a Li complex. Non-limiting examples of the Li complex may be lithium quinolate (LiQ) or the following compound 103, but are not limited thereto.

The hole auxiliary layer 3 may be interposed between the emission layer 5 and anode 1 to increase hole mobility. The hole auxiliary layer 3 may include, for example at least one layer selected from a hole injection layer (HIL), a hole transport layer (HTL), and an electron blocking layer.

The hole injection layer (HIL) may include general hole injection material, for example, a phthalocyanine compound such as copper-phthalocyanine, and the like, m-MTDATA [4,4′,4″-tris(3-methylphenylphenylamino)triphenylamine], NPB (N,N′-di(1-naphthyl)-N,N′-diphenylbenzidine, TDATA, 2T-NATA, Pani/DBSA (polyaniline/dodecylbenzenesulfonic acid), PEDOT/PSS (poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate)), pani/CSA (polyaniline/camphor sulfonic acid) or PANI/PSS (polyaniline)/poly(4-styrenesulfonate)), and the like, but is not limited thereto.

The hole transport layer (HTL) may include a general hole transport layer (HTL) material, for example, a carbazole derivative such as N-phenylcarbazole, polyvinylcarbazole, and the like, an amine derivative having an aromatic condensed ring such as NPB, N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1-biphenyl]-4,4′-diamine (TPD), and the like. For example, in the case of TCTA, it may prevent the diffusion of excitons from the emission layer as well as it may transport a hole.

The hole injection layer (HIL) or the hole transport layer (HTL) may further include a charge-generating material so as to improve film conductivity.

The charge-generating material may be for example, a p-dopant. Non-limiting examples of the p-dopant may include a quinone derivative such as tetracyanoquinone dimethane (TCNQ) and 2,3,5,6-tetrafluoro-tetracyano-1,4-benzoquinonedimethane (F4TCNQ); a metal oxide such as tungsten oxide and molybdenum oxide; and a cyano group-contained compound such as the following compound 100 or the like, but are not limited thereto.

When the hole injection layer (HIL) or the hole transport layer (HTL) further include the charge-generating material, the charge-generating material may be variously modified such as uniformly dispersed in the layers or randomly distributed in the layers.

For example, an organic light emitting diode device according to one embodiment may have a structure of anode/hole injection layer (HIL)/emission layer/cathode, anode/hole injection layer (HIL)/hole transport layer (HTL)/emission layer/electron transport layer (ETL)/cathode, or anode/hole injection layer (HIL)/hole transport layer (HTL)/emission layer/electron transport layer (ETL)/electron injection layer (EIL)/cathode. In addition, the organic light emitting diode device may have a structure of anode/functional layer simultaneously having hole injection function and hole transport function/emission layer/electron transport layer (ETL)/cathode or anode/functional layer simultaneously having a hole injection function and a hole transport function/emission layer/electron transport layer (ETL)/electron injection layer (EIL)/cathode. Alternatively, the organic light emitting diode device may have a structure of anode/hole transport layer (HTL)/emission layer/functional layer simultaneously having electron injection function and electron transport function/cathode, anode/hole injection layer (HIL)/emission layer/functional layer simultaneously having electron injection function and electron transport function/cathode, or anode/hole injection layer (HIL)/hole transport layer (HTL)/emission layer/functional layer simultaneously having electron injection function and electron transport function/cathode structure, but is not limited thereto.

The organic layer 10 may be formed by, for example, various methods such as vacuum deposition, a spin coating, a casting, LB or the like.

When the organic layer is formed by the vacuum deposition, the deposition conditions may be different according to the compound used as the material for the organic layer, the structure of the desired organic layer, and thermal characteristics, but generally, may be appropriately selected within the ranges of deposit temperature of about 100 to about 500° C., the vacuum degree of about 10⁻⁸ to about 10⁻³ torr, and the deposition rate of about 0.01 to about 100 Å/sec, without limitation.

When the organic layer is formed by the spin coating, the coating conditions are different according to the compound used as a material for the organic layer, the structure of the desired organic layer, and thermal characteristics or the like, but may be suitably selected from the ranges of a coating speed of about 2000 rpm to about 5000 rpm, a heat treatment temperature of about 80° C. to about 200° C. for removing the solvent after coating, without limitation.

The organic layer 10 includes a layer including the organic compound represented by the above Chemical Formula 1, and the layer may be an emission layer.

The organic layer 10 may further include at least one layer of a hole injection layer (HIL), a hole transport layer (HTL), an electron blocking layer, a hole blocking layer, an electron transport layer (ETL), and an electron injection layer (EIL) as well as the emission layer.

The organic light emitting diode device may be electrically connected to for example a thin film transistor, and the thin film transistor may be disposed between the substrate and electrode.

In addition, the layer of organic light emitting diode device according to another embodiment may be formed by the deposition using the organic compound according to one embodiment or may be also formed by the wet method of coating the organic compound according to one embodiment in a solution.

Hereinafter, specific synthesis examples and examples illustrate these embodiments in more detail. However, the present disclosure is not limited to these embodiments.

SYNTHESIS EXAMPLES Synthesis Example 1 Synthesis of Chemical Formula 3

Synthesis of Intermediate I-1

3.80 g (20 mmol) of 4H-cyclopenta[def]phenanthrene was put in 20 mL of DMSO and 20 mL of a 50% sodium hydroxide aqueous solution, and 2.96 g (21 mmol) of iodomethane was slowly added thereto. The mixture was reacted at room temperature for 24 hours and three times extracted with 50 mL of water and 50 mL of diethylether. The obtained organic layer was dried with magnesium sulfate, a solvent therein was evaporated, and the obtained residues were separated and purified through silica gel column chromatography, obtaining 3.70 g of an intermediate I-1 (a yield of 85%). The produced compound was identified through MS/FAB. C₁₇H₁₄ (a calculation value: 218.11 g/mol, and a measurement value: 218.15 g/mol)

Synthesis of Intermediate I-2

3.70 g (17.0 mmol) of the intermediate I-1 and 600 mg of 10% palladium charcoal were dissolved in 100 mL of methanol/methylenechloride (1/1 of a volume ratio), and the solution was agitated under a hydrogen pressure (60 psi) for 15 hours. The agitated solution was filtered to remove a catalyst, a solvent therein was evaporated and removed, and the obtained residues were separated and purified through silica gel column chromatography, obtaining 3.52 g of an intermediate I-2 (a yield of 94%). The produced compound was identified through MS/FAB. C₁₇H₁₆ (a calculation value: 220.13 g/mol, and a measurement value: 220.10 g/mol)

Synthesis of Intermediate I-3

20 g of CuBr₂ was dissolved in 60 mL of distilled water, and 40 g of neutralized alumina was added to this aqueous solution at room temperature. Then, a solvent therein was evaporated, and the obtained residue was treated under a condition of 100° C., 4 Torr for 15 hours, obtaining CuBr₂ absorbed in the alumina. 1.54 g (7.00 mmol) of the intermediate I-2 was dissolved in 140 mL of carbon tetrachloride, and 62 g of the CuBr₂ was added thereto at room temperature. The mixture was agitated at 60° C. for 12 hours and filtered, and the obtained solid was cleaned with 60 mL of carbon tetrachloride. The obtained residue was separated and purified through silica gel column chromatography, obtaining 2.14 g of an intermediate I-3 (a yield of 81%). The produced compound was identified through MS/FAB. C₁₇H₁₄Br₂ (a calculation value: 375.95 g/mol, and a measurement value: 376.01 g/mol)

Synthesis of Intermediate I-4

2.14 g (5.66 mmol) of the intermediate I-3 was dissolved in 70 mL of CS₂, and another solution prepared by dissolving 0.32 mL (6.22 mmol) of bromine in CS₂ was slowly added in a dropwise fashion for 3 hours. The mixed solution was agitated for one hour and concentrated under vacuum for one hour, and the obtained residue was separated and purified through silica gel column chromatography, obtaining 1.92 g of an intermediate I-4 (a yield of 90%). The produced compound was identified through MS/FAB. C₁₇H₁₂Br₂ (a calculation value: 373.93 g/mol, and a measurement value: 373.96 g/mol)

Synthesis of Chemical Formula 3

1.92 g (5.10 mmol) of the intermediate I-4, 1.76 g (10.2 mmol) of naphthalene-2-boronic acid, 0.29 g (0.25 mmol) of Pd(PPh₃)₄(tetrakis(triphenylphosphine)palladium), 1.05 g (7.62 mmol) of K₂CO₃ were dissolved in 60 mL of a solution prepared by mixing THF/H₂O in a volume ratio of 2/1), and the obtained solution was agitated at 70° C. for 10 hours. The reaction solution was cooled down to room temperature, 40 mL of water was added thereto, and the mixture was three times extracted with 40 mL of ethylether. The obtained organic layer was dried with magnesium sulfate, and a residue obtained by evaporating a solvent therein was separated and purified through silica gel column chromatography, obtaining 1.79 g of a compound represented by Chemical Formula 3 (a yield of 75%). The produced compound was identified through MS/FAB. C₃₇H₂₆ (a calculation value: 470.20 g/mol, and a measurement value: 470.25 g/mol)

Synthesis Example 2 Synthesis of Chemical Formula 5

2.24 g of a compound represented by Chemical Formula 5 (a yield of 71%) was obtained according to the same method as Synthesis Example 1 of preparing the compound represented by the above Chemical Formula 3 by using pyrene-1-boronic acid instead of naphthalene-2-boronic acid. The produced compound was identified through MS/FAB. C₄₉H₃₂ (a calculation value: 620.25 g/mol, and a measurement value: 620.20 g/mol)

Synthesis Example 3 Synthesis of Chemical Formula 13

2.24 g of a compound represented by Chemical Formula 13 (a yield of 78%) was obtained according to the same method as Synthesis Example 1 of preparing the compound represented by the above Chemical Formula 3 by using the intermediate I-5 instead of naphthalene-2-boronic acid. The produced compound was identified through MS/FAB. C₅₇H₃₈ (a calculation value: 722.30 g/mol, and a measurement value: 722.28 g/mol)

Synthesis Example 4 Synthesis of Chemical Formula 35

Synthesis of Intermediate I-6

10.0 g (52.6 mmol) of 4H-cyclopenta[def]phenanthrene and 8.40 g of 5% Pd/C were dissolved in 70 mL of EtOH in a Par reactor bottle, and the solution was agitated at room temperature for 24 hours, while its hydrogen pressure was maintained at 40 psi. When the reaction was complete, the reaction solution was filtered, and a solvent therein was evaporated, obtaining 8.60 g of an intermediate I-6 (a yield of 85%). The produced compound was identified through MS/FAB. C₁₅H₁₂ (a calculation value: 192.09 g/mol, and a measurement value: 192.11 g/mol)

Synthesis of Intermediate I-7

8.50 g (44.2 mmol) of the intermediate I-6 was dissolved in 80 mL of CCl₄, and 14.2 g (88.4 mmol) of Br₂ was slowly added thereto in a dropwise fashion at 0° C. The reaction solution was agitated at room temperature for 4 hours, and a 10% Na₂SO₃ solution was added thereto, obtaining an organic layer. The organic layer was dried with magnesium sulfate and then, recrystallized with n-hexane after evaporating a solvent therein, obtaining 8.9 g of an intermediate I-7 (a yield of 57%). The produced compound was identified through MS/FAB. C₁₅H₁₀Br₂ (a calculation value: 347.91 g/mol, and a measurement value: 347.88 g/mol)

Synthesis of Intermediate I-8

8.9 g (25.4 mmol) of the intermediate I-7 and 6.6 g (27.0 mmol) of o-chloranil were dissolved in 70 mL of Xylene, and the solution was agitated at 110° C. for 72 hours. The reaction solution was cooled down to room temperature, and a residue obtained by evaporating a solvent therein was separated and purified through silica gel column chromatography, obtaining 7.16 g of an intermediate I-8 (a yield of 81%). The produced compound was identified through MS/FAB. C₁₅H₈Br₂ (a calculation value: 345.90 g/mol, and a measurement value: 345.87 g/mol).

Synthesis of Intermediate I-9

7.16 g (20.6 mmol) of the intermediate I-8 and 280 g of MnO₂ were dissolved in 200 mL of benzene, and the solution was agitated at 80° C. for 20 hours. The reaction solution was cooled down to room temperature, filtered to remove MnO₂, and cleaned with CHCl₃ (50 mL), THF (50 mL), and MeOH (50 mL) in order. The filtered solution was evaporated, and the obtained residue was recrystallized with acetone, obtaining 3.73 g of an intermediate I-9 (a yield of 50%). The produced compound was identified through MS/FAB. C₁₅H₆Br₂O (a calculation value: 359.88 g/mol, and a measurement value: 359.91 g/mol)

Synthesis of Intermediate I-10

2.40 g (10.3 mmol) of 2-bromo biphenyl was dissolved in 50 mL of THF, and 12.1 mL (20.6 mmol, 1.7M in pentane) of t-BuLi was slowly added thereto in a dropwise fashion at −78° C. The mixture was agitated for one hour at the same temperature, 3.73 g (10.3 mmol) of the intermediate I-9 was slowly added in a dropwise fashion for 30 minutes, and the reaction solution was agitated at −78° C. for 30 minutes and additionally agitated for 3 hours. Then, 40 mL of water was added to the reaction solution and three times extracted with 50 mL of ethylacetate. The organic layer was dried with magnesium sulfate, and a residue obtained by evaporating a solvent therefrom was separated and purified through silica gel column chromatography, obtaining a 4.66 g of an intermediate I-10 (a yield of 93%). The produced compound was identified through MS/FAB. C₂₇H₁₆Br₂O (a calculation value: 513.96 g/mol, and a measurement value: 514.01 g/mol)

Synthesis of Intermediate I-11

4.66 g (9.03 mmol) of the intermediate I-10 was dissolved in 50 mL of acetic acid, 3 mL of concentrated hydrochloric acid was slowly added thereto in a dropwise fashion at 0° C., and the mixture was agitated for 2 hours. A white solid produced during the reaction was filtered and cleaned with acetic acid and ethanol, obtaining 4.05 g of an intermediate I-11 (a yield of 90%). The produced compound was identified through MS/FAB. C₂₇H₁₄Br₂ (a calculation value: 495.95 g/mol, and a measurement value: 496.01 g/mol)

Synthesis of Chemical Formula 35

2.51 g of a compound represented by Chemical Formula 35 (a yield of 66%) was obtained according to the same method as the synthesis example of preparing the compound 2 by using the intermediate I-11 instead of the intermediate I-4 and the intermediate I-12 instead of the naphthalene-2-boronic acid. The produced compound was identified through MS/FAB. C₅₇H₃₄N₂ (a calculation value: 746.27 g/mol, and a measurement value: 746.30 g/mol)

Synthesis Example 5 Synthesis of Chemical Formula 46

Synthesis of Intermediate I-13

5.49 g (14.6 mmol) of the intermediate I-4, 5.55 g (14.6 mmol) of the intermediate I-5, 0.84 g (0.73 mmol) of Pd(PPh₃)₄, and 6.05 g (43.8 mmol) of K₂CO₃ were dissolved in 60 mL of THF and 40 mL of H₂O, and the solution was agitated at 80° C. for 24 hours. The reaction solution was cooled down to room temperature, 50 mL of water was added thereto, and the mixture was three times extracted with 50 mL of ethylether. The organic layer was dried with magnesium sulfate, and a residue obtained by evaporating a solvent therein was separated and purified through silica gel column chromatography, obtaining 5.37 g of an intermediate I-13 (a yield of 67%). The produced compound was identified through MS/FAB. C₃₇H₂₅Br (a calculation value: 548.11 g/mol, a measurement value: 548.08 g/mol)

Synthesis of Chemical Formula 46

2.80 g (5.10 mmol) of the intermediate I-13, 1.13 g (5.10 mmol) of phenanthrene-9-boronic acid, 0.29 g (0.25 mmol) of Pd(PPh₃)₄, and 1.05 g (7.26 mmol) of K₂CO₃ were dissolved in 60 mL of THF and 40 mL of H₂O, and the solution was agitated at 80° C. for 24 hours. The reaction solution was cooled down to room temperature, 50 mL of water was added thereto, and the mixture was three times extracted with 50 mL of ethylether. The obtained organic layer was dried with magnesium sulfate, and a residue obtained by evaporating a solvent therein was separated and purified through silica gel column chromatography, obtaining 2.67 g of a compound represented by Chemical Formula 46 (a yield of 81%). The produced compound was identified through MS/FAB. C₅₁H₃₄ (a calculation value: 646.27 g/mol, and a measurement value: 646.30 g/mol)

Additional compounds were synthesized by using appropriate intermediate materials using the same synthesis method as the synthesis process, and the following Table 1 shows ¹H NMR and MS/FAB of the compounds.

Other compounds than the compound in Table 1 may be easily synthesized with a reference to the aforementioned processes and raw materials by those who are skilled and knowledgeable in a related art.

TABLE 1 MS/FAB Chemical Measurement Calculation Formula ¹H NMR (CDCl₃, 400 MHz) value value 3 d = 8.15-8.13 (m, 2H), 8.06-8.04 (m, 2H), 8.00-7.99 (m, 1H), 470.25 470.20 7.97-7.96 (m, 1H), 7.95-7.93 (m, 1H), 7.92-7.89 (m, 3H), 7.84-7.82 (m, 1H), 7.81-7.80 (m, 1H), 7.67-7.66 (m, 2H), 7.61-7.57 (m, 2H), 7.54-7.49 (m, 4H) 1.83 (s, 6H) 5 d = 8.16-8.14 (dd, 2H), 8.11-8.10 (m, 2H), 8.07-8.06 (m, 2H), 620.20 620.25 8.03-8.01 (m, 4H), 7.98-7.96 (m, 2H), 7.93-7.92 (m, 1H), 7.90-7.89 (m, 2H), 7.87-7.86 (m, 2H), 7.83 (s, 2H), 7.79 (s, 1H) 7.70-7.69 (m, 2H), 7.64 (d, 2H), 7.51-7.50 (m, 1H), 7.47-7.46 (m, 1H), 1.84 (s, 6H) 7 d = 8.20-8.19 (m, 2H), 8.11-8.10 (m, 2H), 8.00-7.98 (m, 2H), 594.19 594.23 7.96-7.93 (m, 2H), 7.87-7.84 (m, 4H), 7.64-7.59 (m, 2H), 7.56-7.52 (m, 2H), 7.44 (d, 2H), 7.42-7.41 (m, 2H) 7.36-7.30 (m, 4H), 7.20-7.14 (m, 6H) 9 d = 8.13-8.11 (dd, 2H), 8.06-8.04 (m, 2H), 7.93-7.91 (m, 1H), 622.30 622.27 7.90-7.88 (m, 1H), 7.87-7.86 (m, 2H), 7.84-7.82 (m, 2H), 7.77-7.74 (m, 2H), 7.73-7.70 (m, 4H) 7.66-7.64 (m, 2H), 7.63-7.59 (m, 6H), 7.55-7.51 (m, 4H), 1.83 (s, 6H) 13 d = 8.20-8.18 (m, 2H), 7.82-7.77 (m, 10H), 7.67 (d, 2H), 722.28 722.30 7.52-7.51 (dd, 2H), 7.50-7.45 (m, 6H), 7.41-7.39 (m, 3H), 7.38-7.37 dd, 2H), 7.36 (d, 1H), 7.32 (d, 1H), 7.30-7.29 (dd, 2H), 7.28 (d, 1H), 1.82 (s, 6H) 19 d = 8.13-8.11 (m, 4H), 7.93-7.92 (m, 1H), 7.91-7.90 (m, 1H), 550.21 550.19 7.85 (d, 1H), 7.83 (d, 1H), 7.73-7.71 (m, 1H), 7.70-7.69 (m, 1H), 7.67-7.64 (m, 4H), 7.55-7.52 (m, 2H), 7.42 (d, 2H), 7.35-7.31 (m, 2H), 1.84 (s, 6H) 23 d = 8.11-8.09 (m, 2H), 7.64-7.63 (m, 2H), 7.61-7.58 (m, 4H), 514.22 514.25 7.54-7.51 (m, 4H), 7.39 (d, 2H), 1.83 (s, 6H), 0.36 (s, 18H) 26 d = 8.21-8.20 (dd, 2H), 7.82-7.78 (m, 6H), 7.66 (d, 2H), 732.38 732.36 7.52-7.51 (dd, 2H), 7.50-7.49 (dd, 2H), 7.39 (d, 1H), 7.38 (d, 2H), 7.35 (d, 1H), 7.31-7.28 (m, 4H), 1.83 (s, 6H) 30 d = 8.21-8.19 (m, 2H), 8.13-8.12 (m, 2H), 8.06-8.05 (m, 2H), 622.25 622.27 7.99-7.97 (m, 2H), 7.96-7.94 (m, 2H), 7.83-7.82 (m, 1H), 7.81-7.80 (m, 1H), 7.71 (d, 1H), 7.69 (d, 1H), 7.67-7.66 (m, 2H), 7.63-7.60 (m, 4H), 7.52 (d, 2H), 7.49-7.46 (m, 3H), 7.45-7.44 (m, 1H), 7.42-7.39 (m, 2H), 1.84 (s, 6H) 35 d = 8.45 (d, 2H), 8.28-8.27 (m, 2H), 8.12-8.10 (dd, 2H), 746.30 746.27 8.04-8.03 (dd, 2H), 8.01-7.99 (m, 2H), 7.95-7.93 (m, 5H), 7.91-7.83 (m, 5H), 7.67 (s, 2H), 7.61-7.57 (m, 4H), 7.44 (t, 2H), 7.20 (t, 2H), 7.06 (d, 2H), 6.91-6.89 (dd, 2H) 37 d = 8.21-8.20 (m, 2H), 8.15-8.14 (m, 1H), 8.13-8.12 (m, 1H), 734.20 734.21 8.10-8.09 (m, 1H), 8.08-8.07 (m, 1H), 8.02-8.01 (m, 2H), 7.82 (d, 1H), 7.81-7.80 (m, 2H), 7.78-7.77 (m, 1H), 7.75-7.72 (m, 4H), 7.71-7.68 (m, 4H), 7.63-7.62 (m, 2H), 7.53 (d, 2H), 7.46-7.42 (m, 2H), 7.38-7.35 (m, 2H), 1.83 (s, 6H) 40 d = 8.24-8.22 (dd, 2H), 8.01-8.00 (m, 2H), 7.94-7.92 (m, 2H), 828.41 828.37 7.91-7.88 (m, 6H), 7.80-7.79 (m, 2H), 7.77-7.76 (dd, 2H), 7.75-7.74 (m, 2H), 7.65 (d, 2H), 7.62-7.60 (m, 2H), 7.59-7.55 (m, 6H), 7.40-7.34 (m, 8H) 45 d = 8.17-8.16 (dd, 2H), 8.07-8.06 (m, 2H), 7.94-7.93 (m, 1H), 622.25 622.27 7.92-7.91 (m, 1H), 7.87-7.85 (m, 3H), 7.83-7.81 (m, 3H), 7.71 (d, 1H), 7.69 (d, 1H), 7.67-7.66 (m, 2H), 7.62-7.58 (m, 2H), 7.55-7.47 (m, 8H), 7.20-7.17 (tt, 2H), 1.83 (s, 6H) 46 d = 8.27-8.25 (m, 1H), 8.20-8.18 (m, 1H), 8.13-8.12 (dd, 1H), 646.30 646.27 8.09-8.08 (dd, 1H), 7.82-7.77 (m, 7H), 7.70-7.69 (m, 1H), 7.67-7.63 (m, 4H), 7.54-7.46 (m, 6H), 7.41-7.36 (m, 3H), 7.32-7.28 (m, 2H), 7.18-7.14 (m, 1H), 1.84 (s, 6H) 52 d = 8.22-8.21 (m, 1H), 8.15-8.14 (m, 1H), 8.08-8.06 (m, 2H), 585.23 585.25 8.00-7.98 (m, 1H), 7.96-7.93 (m, 2H), 7.87-7.83 (m, 2H), 7.71-7.70 (m, 1H), 766-7.65 (m, 2H), 7.63-7.58 (m, 3H), 7.53-7.49 (m, 6H), 7.39-7.28 (m, 3H), 7.22-7.20 (m, 1H), 1.83 (s, 6H) 58 d = 8.45-8.44 (m, 2H), 8.31-8.29 (m, 2H), 8.20-8.18 (m, 2H), 700.31 700.29 8.07-8.04 (tt, 2H), 7.93-7.92 (m, 1H), 7.86-7.85 (m, 2H), 7.80-7.76 (m, 5H), 769-7.66 (m, 2H), 7.55-7.52 (m, 2H), 7.50-7.46 (m, 5H), 7.41-7.36 (m, 3H), 7.33-7.28 (m, 2H), 1.84 (s, 6H) 60 d = 8.49-8.47 (dd, 1H), 8.25-8.24 (m, 1H), 8.21-8.19 (dd, 1H), 647.25 647.26 8.14-8.12 (m, 2H), 8.07-8.06 (m, 1H), 8.01-7.99 (m, 1H), 7.94-7.90 (m, 5H), 7.76-7.74 (m, 3H), 7.66 (d, 1H), 7.62-7.58 (m, 4H), 7.56-7.52 (m, 2H), 7.47-7.44 (m, 1H), 7.40-7.33 (m, 4H), 1.83 (s, 6H) 66 d = 8.53-8.52 (dd, 1H), 8.42-8.40 (m, 5H), 8.33-8.31 (m, 1H), 701.30 701.28 8.24-8.22 (m, 1H), 8.17-8.15 (dd, 1H), 8.09-8.07 (m, 1H), 7.90-7.86 (m, 2H), 7.79-7.75 (m, 3H), 7.69-7.59 (m, 7H), 7.54-7.50 (m, 4H), 7.42-7.38 (m, 2H), 7.16-7.13 (m, 1H), 1.84 (s, 6H) 70 d = 8.52-8.51 (m, 2H), 8.44 (d, 1H), 8.40 (d, 1H), 8.32-8.30 (m, 744.30 744.28 2H), 8.23-8.20 (m, 2H), 8.17 (d, 1H), 8.13-8.12 (m, 1H), 8.09-8.08 (m, 1H), 8.05 (d, 2H), 7.98-7.89 (m, 5H), 7.82-7.80 (m, 1H), 7.71-7.69 (m, 1H), 7.62-7.60 (m, 2H), 7.50-7.41 (m, 7H), 7.25-7.22 (tt, 2H), 7.10-7.09 (m, 1H), 7.04-7.02 (dd, 2H)

EXAMPLES Example 1

15 Ω/cm² (1200 Å) ITO glass substrate (manufactured by Corning) was cut in a size of 50 mm×50 mm×0.7 mm and cleaned with ultrasonic wave using isopropyl alcohol and pure water for each 5 minutes, and then irradiated with ultraviolet (UV) for about 30 minutes and cleaned by exposing ozone. 2-TNATA was vacuum deposited on the ITO glass substrate to form a hole injection layer (HIL) having a thickness of 600 Å, and 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (hereinafter, NPB) was vacuum deposited to form a hole transport layer (HTL) having a thickness of 300 Å.

The following Chemical Formula 5 as a blue fluorescent host and 4,4′-bis[2-(4-(N,N-diphenylamino)phenyl)vinyl]biphenyl (hereinafter, DPAVBi) as a blue fluorescent dopant were co-deposited on the hole transport layer (HTL) in a weight ratio of 98:2 to form a 300 Å-thick emission layer.

Then, Alq₃ was deposited on the emission layer in a thickness of 300 Å to form an electron transport layer (ETL) and LiF was deposited on the electron transport layer (ETL in a thickness of 10 Å to form an electron injection layer (EIL). Al was vacuum deposited on the electron injection layer (EIL) in a thickness of 3000 Å to form a cathode and thus organic light emitting diode device was manufactured.

Example 2

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using the following Chemical Formula 13 to form an emission layer, instead of the compound 4.

Example 3

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using the Chemical Formula 30 to form an emission layer, instead of the compound 4.

Example 4

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using the Chemical Formula 35 to form an emission layer, instead of the compound 4.

Example 5

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using the Chemical Formula 40 to form an emission layer, instead of the compound 4.

Example 6

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using the Chemical Formula 46 to form an emission layer, instead of the compound 4.

Example 7

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using 9,10-di-naphthalen-2-yl-anthracene (hereinafter, DNA) to form an emission layer, instead of the compound 4 and using the following Chemical Formula 58 to form an electron transport layer (ETL), instead of Alq₃.

Example 8

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 7, except using the following Chemical Formula 66 to form an electron transport layer (ETL), instead of the compound 57.

Comparative Example 1

An organic light emitting diode device was manufactured in accordance with the same procedure as in Example 1, except using a blue fluorescent host, DNA to form an emission layer, instead of the compound 4.

Evaluation

The characteristics of organic light emitting diode devices obtained from Examples 1 to 8 and Comparative Example 1 were evaluated.

The results are shown in Table 2.

TABLE 2 Light emitting material or half life- electron Driving Current Light span transport voltage density Luminance Efficiency emitting (hr material (V) (mA/cm²) (cd/m²) (cd/A) color @100 mA/cm²) Example 1 Chemical 6.36 50 3,205 6.41 blue 304 hr Formula 5 Example 2 Chemical 6.23 50 3,175 6.35 blue 326 hr Formula 13 Example 3 Chemical 6.25 50 3,145 6.29 blue 313 hr Formula 30 Example 4 Chemical 6.46 50 3,035 6.07 blue 288 hr Formula 35 Example 5 Chemical 6.19 50 3,165 6.33 blue 323 hr Formula 40 Example 6 Chemical 6.17 50 3,115 6.23 blue 307 hr Formula 46 Example 7 Chemical 5.17 50 3,235 6.47 blue 413 hr Formula 58 Example 8 Chemical 5.25 50 3,315 6.63 blue 435 hr Formula 66 Comparative DNA 7.35 50 2,065 4.13 blue 145 hr Example 1

Referring to Table 2, the organic light emitting diode devices according to Examples 1 to 8 showed all improved driving voltage, luminance, efficiency, and life-span characteristic compared with the organic light emitting diode device according to Comparative Example 1.

When the compounds according to Examples 1 to 8 were all applied as a host material of a blue emission layer and an electron transport material to an organic light emitting diode device, the compounds improved driving voltage and efficiency of the organic light emitting diode device compared with a conventional material, DNA and Alq₃ and realized excellent I-V-L characteristic and in particular, remarkably improved life-span.

While these embodiments have been described in connection with what is presently considered to be practical example embodiments, it is to be understood that the embodiments are not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Therefore, the aforementioned embodiments should be understood to be examples but not limiting this disclosure in any way. 

What is claimed is:
 1. An organic compound represented by the following Chemical Formula 1:

wherein, in the above Chemical Formula 1, R₁ and R₂ are each independently hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, R₃ to R₅ are each independently hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, n is an integer ranging from 0 to 2, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.
 2. The organic compound of claim 1, wherein in the above Chemical Formula 1, R₁ and R₂ are each independently a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.
 3. The organic compound of claim 1, wherein in the above Chemical Formula 1, R₁ and R₂ are each independently a substituted or unsubstituted C₁ to C₃₀ alkyl group, or a substituted or unsubstituted C₁ to C₃₀ aryl group, or R₁ and R₂ are linked to each other to form a ring, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted phenyl group, a substituted or unsubstituted biphenyl group, a substituted or unsubstituted terphenyl group, a substituted or unsubstituted naphthalene group, a substituted or unsubstituted anthracene group, a substituted or unsubstituted phenanthrene group, a substituted or unsubstituted pyrene group, a substituted or unsubstituted fluorene group, a substituted or unsubstituted carbazole group, a substituted or unsubstituted dibenzofuran, a substituted or unsubstituted dibenzothiophene, a substituted or unsubstituted pyridine group, or a combination thereof.
 4. The organic compound of claim 1, wherein the compound represented by the above Chemical Formula 1 is an organic compound including at least one selected from the compound listed in the following Group 1:


5. The organic compound of claim 1, wherein the compound represented by the above Chemical Formula 1 is an organic compound including at least one selected from the following:


6. An organic light emitting diode device, comprising an anode, a cathode, and an organic layer interposed between the anode and cathode wherein the organic layer comprises an organic compound represented by the following Chemical Formula 1:

wherein, in the above Chemical Formula 1, R₁ and R₂ are each independently hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, R₃ to R₅ are each independently hydrogen, deuterium, a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₂ to C₃₀ alkenyl group, a substituted or unsubstituted C₂ to C₃₀ alkynyl group, a substituted or unsubstituted C₃ to C₃₀ cycloalkyl group, a substituted or unsubstituted C₁ to C₃₀ alkoxy group, a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, a halogen, a cyano group, a nitro group, a hydroxy group, a carboxyl group, or a combination thereof, n is an integer ranging from 0 to 2, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted C₆ to C₃₀ aryloxy group, a substituted or unsubstituted C₆ to C₃₀ arylthiol group, a substituted or unsubstituted C₆ to C₃₀ aryl group, an amino group substituted with a C₆ to C₃₀ aryl group or a C₂ to C₃₀ heteroaryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.
 7. The organic light emitting diode device of claim 6, wherein the R₁ and R₂ are each independently a substituted or unsubstituted C₁ to C₃₀ alkyl group, a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof, or R₁ and R₂ are linked to each other to form a ring, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted C₆ to C₃₀ aryl group, a substituted or unsubstituted C₂ to C₃₀ heteroaryl group, or a combination thereof.
 8. The organic light emitting diode device of claim 6, wherein the R₁ and R₂ are each independently a substituted or unsubstituted C₁ to C₃₀ alkyl group, or a substituted or unsubstituted C₁ to C₃₀ aryl group, or R₁ and R₂ are linked to each other to form a ring, and Ar₁ and Ar₂ are each independently a substituted or unsubstituted phenyl group, a substituted or unsubstituted biphenyl group, a substituted or unsubstituted terphenyl group, a substituted or unsubstituted naphthalene group, a substituted or unsubstituted anthracene group, a substituted or unsubstituted phenanthrene group, a substituted or unsubstituted pyrene group, a substituted or unsubstituted fluorene group, a substituted or unsubstituted carbazole group, a substituted or unsubstituted dibenzofuran, a substituted or unsubstituted dibenzothiophene, a substituted or unsubstituted pyridine group, or a combination thereof.
 9. The organic light emitting diode device of claim 6, wherein the organic layer comprises at least one organic compound selected from the compounds listed in the following Group 1:


10. The organic light emitting diode device of claim 6, wherein the compound represented by the above Chemical Formula 1 is an organic compound including at least one selected from the following:


11. The organic light emitting diode device of claim 6, wherein the organic layer comprises an emission layer, and the organic compound represented by the above Chemical Formula 1 is included in the emission layer.
 12. The organic light emitting diode device of claim 11, wherein the emission layer further comprises anthracene, arylamine, styrene, a derivative thereof, or a combination thereof.
 13. The organic light emitting diode device of claim 11, wherein the emission layer comprises the organic compound represented by the above Chemical Formula 1 as a fluorescent or phosphorescent host.
 14. The organic light emitting diode device of claim 6, wherein the organic layer comprises an emission layer, and an auxiliary layer interposed between the emission layer and the cathode, and the organic compound represented by the above Chemical Formula 1 is included in the auxiliary layer.
 15. The organic light emitting diode device of claim 14, wherein the emission layer comprises anthracene, arylamine, styrene, a derivative thereof, or a combination thereof. 